大孔磺酸树脂催化剂催化FCC汽油烷基化脱硫反应失活原因分析

采用"BA试验"方法进行大孔磺酸树脂催化剂催化FCC汽油烷基化脱硫反应的加速寿命试验考察;通过BET比表面积、非金属元素分析和FT-IR等分析技术研究烷基化脱硫催化剂失活的原因,并对失活催化剂浸取物进行分析。结果表明,经过多次深处理后,催化剂活性基本丧失。在反应过程中,烯烃低聚和芳烃烷基化等副反应生成的高分子有机副产物覆盖催化剂的活性中心以及碱性氮化物中和活性基团H+是造成催化剂活性降低的原因,并且高分子有机副产物覆盖催化剂的活性中心为主要原因。覆盖催化剂或堵塞孔道的物质主要由大量长链烷烃、少量长链烯烃和芳烃物等有机物组成。     

循环流化床锅炉脱硫技术

介绍了我国循环流化床锅炉脱硫现状,重点讨论了循环流化床锅炉炉内喷钙脱硫技术、炉内喷钙烟气半干法脱硫技术和炉内喷钙烟气湿法脱硫技术。结合现有的环保政策和脱硫成本,炉内喷钙脱硫技术难以满足现有环保要求;对燃用低硫煤循环流化床锅炉,建议采用炉内喷钙烟气半干法脱硫技术,该技术可以满足环保要求,且脱硫成本较低;对燃用高硫煤循环流化床锅炉,建议采用炉内喷钙烟气湿法脱硫技术,该技术能满足环保要求,但脱硫成本较高。     

FCC汽油选择性加氢脱硫催化剂Ru/Al_2O_3的研究

以900℃焙烧的Al_2O_3为载体,用浸渍法制备了蛋壳型Ru催化剂,Ru的负载质量分数为3%,并对催化剂进行了BET和XRD表征。催化剂活性评价在高压微反装置上进行,以FCC汽油为原料,评价前催化剂预硫化。结果表明,400℃高温焙烧会造成Ru的烧结,不焙烧(仅120℃干燥6h)的催化剂具有较高活性,对于FCC汽油的选择性加氢脱硫,在300℃、2.0MPa、空速2h~(-1)和氢油体积比=200:1条件下,FCC汽油的加氢脱硫率达66.4%,烯烃加氢饱和率达24.7%,选择性因子仅为3.8。单组分Ru催化剂用于FCC汽油的加氢脱硫时有一定的选择性,但结果不理想。     

碳纳米管的表面修饰对Co-Mo催化剂HDS性能影响的研究

采用程序升温脱附(TPD)、Boehm滴定以及质量滴定(Masstitration)等方法分析了多壁碳纳米管(MWCNT)经过浓硝酸改性处理前后的表面酸性和酸性分布;同时运用XRD技术研究了碳纳米管负载Co Mo催化剂的表面物种和活性组分的分散;并在高压微型反应器中,以二苯并噻吩(DBT)为模型化合物,对碳纳米管负载的Co Mo催化剂体系进行了加氢脱硫(HDS)活性评价,以期揭示碳纳米管的表面修饰对其负载Co Mo催化剂HDS性能的影响。研究结果表明:MWCNT表面呈一定的碱性,通过浓硝酸化学修饰以后,反而呈现较强的酸性,并且随着酸处理时间的延长,表面的酸性进一步增加。如,M MWCNT 6(酸化6h)表面总酸量为1.29×10-3mol/g,M MWCNT 24(酸化24h)表面总酸量为2.46×10-3mol/g。酸改性提高了Co Mo催化剂在MWCNT表面的分散程度,以致Co Mo/MWCNT催化剂的HDS活性和选择性明显高于Co Mo/γ Al2O3催化体系。然而,Co Mo/M MWC NT 6的HDS活性以及选择性与Co Mo/MWCNT相差不多,略有降低,但是仍比Co Mo/γ Al2O3催化体系的HDS活性高。Co Mo/M MWCNT 24催化剂的HDS活性降低很多,并且催化性能发生了很大改变,产物中出现了大量的副产物1,2 二苯基乙烷。表明,深度酸化改性反而不利于提高碳纳米管负载Co Mo催化体系的HDS活性。     

煤气化－蒸汽联合循环发电（IGCC）技术中的高温煤气热脱硫

本文论述了开发煤气化－蒸汽联合循环发电（ＩＧＣＣ）技术的重要意义。着重分析了国外高温煤气热脱硫方面的研究状况，并结合国内实际情况，指出了我国在开发高温煤气热脱硫技术研究时，应从脱硫剂物系选择、温区划定、反应器选型和实施步骤等方面采取的一系列系统优化政策。     

Microbial desulfurization for NR ground rubber by Thiobacillus ferrooxidans

This study concentrated on microbial desulfurization for NR ground rubber by Thiobacillus ferrooxidans with sulfur oxidizing capacity. NR ground rubber was desulfurizated in the modified 9K medium during the cultivation of T. ferrooxidans. FTIR–ATR and XPS spectra and the increase of SO in the medium indicated that the main chains of the polymer were not broken by T. ferrooxidans, and S? S linkages on the surface of ground rubber were partly oxidized to sulfoxide and sulfone, and at last partly oxidized to SO. Cumulative sulfur convention of ground rubber was 16% (w/w), which means 16% of sulfur has been fully oxidized to SO after 20 days' incubation. A sulfur oxidative scheme was proposed to explain the microbial desulfurization by T. ferrooxidans. Physical properties were determined on carbon black enforced SBR vulcanizates compounded with desulfurizated ground rubber of 40 phr loading. Preferable tensile strength and elongation at break were obtained for SBR vulcanizates filled with desulfurizated ground rubber if compared with that one obtained using ground rubber without modification. Scanning electron microscope photographs and DMA results suggested good interface coherence between desulfurizated ground rubber and SBR matrix. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

多级多尺度烟气脱硫液柱塔的性能研究

为了探索液柱塔的最佳脱硫条件,以多级多尺度液柱塔为研究对象,采用压力旋转和扇形喷嘴进行喷射实验,得到液滴直径分布规律,并探索各因素对其脱硫效率的影响。研究结果表明:脱硫效率随着塔内风速、吸收液pH值、SO2入口浓度的增大而降低,随液气比增大而增大。采用不同喷嘴组合可以有效改善脱硫浆液的雾化效果,解决气液接触时间短以及雾沫夹带问题。在液气比1.5 L.m-3、SO2入口质量浓度300 mg.m-3条件下,脱硫效率可以达到96.5%。